20CrMnMo chemical composition and mechanical properties
Chemical composition
Mass fraction (%): Carbon C: 0.17 ~ 0.23 Silicon Si: 0.17 ~ 0.37 Manganese Mn: 0.90 ~ 1.20 Sulfur S: allow the residual content ≤ 0.035 Phosphorus P: allow the residual content ≤ 0.035 Chromium Cr: 1.10 ~ 1.40 Ni: to allow the residual content ≤ 0.030 Cu: to allow the residual content ≤ 0.030 Molybdenum Mo: 0.20 ~ 0.30 Mechanical Properties
[Sample blank size] 15mm [Heat treatment] Quenching temperature (° C): 850; coolant: oil Tempering heating temperature (° C): 200; coolant: water, air Mechanical Properties Tensile strength (σb / MPa): ≥ 1180 Yield Point (σs / MPa): ≥ 885 Elongation rate (δ5 /%): ≥ 10 Section shrinkage (ψ /%): ≥ 45 Impact absorbed energy (Aku2 / J): ≥ 55 Brinell hardness (HBS100/3000) (annealing or tempering state): ≤ 217 Delivery status: to heat treatment (normalizing, annealing or high-temperature tempering) or without heat treatment delivery, the delivery status should be in the contract
Indicate. |