20CrNiMoA chemical composition and mechanical properties
Chemical Composition
Carbon C: 0.17 ~ 0.23 Silicon Si: 0.17 ~ 0.37 Manganese Mn: 0.60 ~ 0.95 Sulfur S: allow the residual content ≤ 0.035 Phosphorus P: allow the residual content ≤ 0.035 Chromium Cr: 0.40 ~ 0.70 Nickel Ni: 0.35 ~ 0.75 Cu: to allow the residual content ≤ 0.030 Molybdenum Mo: 0.20 ~ 0.30
Mechanical Properties