34CrMo4 chemical composition and mechanical properties
Chemical Composition Carbon C: 0.30 ~ 0.37 Silicon Si: 0.10 ~ 0.40 Manganese Mn: 0.60 ~ 0.90 Sulfur S: allow the residual content ≤ 0.035 Phosphorus P: allow the residual content ≤ 0.035 Chromium Cr: 0.90 ~ 1.20 Ni: to allow the residual content ≤ 0.030 Cu: to allow the residual content ≤ 0.030 Molybdenum Mo: 0.15 ~ 0.30 Mechanical Properties Tensile strength σb (MPa): ≥ 985 (100) Yield strength σs (MPa): ≥ 835 (85) Elongation δ5 (%): ≥ 12 Reduction of area ψ (%): ≥ 45 Impact energy Akv (J): ≥ 63 Impact toughness value of alpha kv (J/cm2): ≥ 78 (8) Hardness: ≤ 229HB Sample size: Sample size is 25mm rough |