3Cr2W8V chemical composition
Chemical composition
Perform standard GB/T1299-2000. Unified digital A20502; Grades 3Cr2W8V; Chemical Composition%: C0.30 ~ 0.40, Si ≤ 0.40, Mn ≤ 0.40, Cr2.20 ~ 2.70, W7.50 ~ 9.00, V0.20 ~ 0.50, p ≤ 0.030, S ≤ 0.030;
Mechanical properties:
Hardness: annealing, 255 ~ 207HB, indentation diameter 3.8 ~ 4.2mm Heat treatment and use
Heat treatment: (Delivery Status: Brinell hardness HBW10/3000 (≤ 255 ~~ 207)), quenching: 1075 to 1125, coolant
: Oil; Uses: used steel casting molds. Lower carbon content, high toughness and good thermal conductivity; contains more
Carbide-forming elements chromium, tungsten, vanadium, and the phase transition temperature is increased, so that the steel has a high temperature strength, hardness, and good thermal fatigue resistance
; Hardenability. Suitable for the manufacture of high temperature, high stress, but not shock loading of the die-casting of copper, aluminum, magnesium alloy with attached mold core, the gate
Sets, split nails, high should beat wax, hot shears, hot forging mold, flat forging machine punch, insert, etc.
|