HARDOX500 material resolved

HARDOX500 Sweden SSAB welding of wear-resistant steel
"1" HARDOX defended by up to 500 500HB Brinell hardness wear-resistant steel, mainly used in anti-wear conditions.
"2" HARDOX500 defended by up to wear-resistant steel Application: crushing machine, sieve, into the feeder, feed hopper, hoist blade plate conveyors, bucket, blades, gears, sprockets.
"3" HARDOX500 defended by up to wear-resistant steel: "fine grain steels.
    The "4" HARDOX500 defended by up to wear-resistant steel hardness :4-32MM = 470-530HBW.32-80MM = 450-540HBW.
5 "HARDOX500 defended by up to wear-resistant steel, mechanical properties: yield strength Re = 1250MPa (no mandatory). Elongation A5 = 10% (20 mm thick steel plate typical value).
"6" HARDOX500 defended by up to wear-resistant steel, impact toughness: Test temperature: -40 (-40F) ° C. Longitudinal Charpy-V impact energy = 45J (20 mm thickness steel plate typ). Charpy-V impact energy transverse 27J / +20 ℃.
"HARDOX500 defended by up to wear steel Delivery Status: quenching.
"8" HARDOX500 defended by up to wear-resistant steel, the implementation of standards: EN 10 204 - 3.1.
"9" HARDOX500 product applications:
"10" due to both the high hardness, high strength and high toughness, serious occasion for those who wear the HARDOX defended wear plates, apparently is the ideal choice. Extend the high wear resistance of steel dump truck body, the excavator bucket crusher and similar equipment life.
"11", the hardness of the steel sheet is effective hardening process by water quenching Online. This method can obtain a high hardness, but also to maintain the low alloy steel component. Outputs wear plates are easy to machining, bending and welding.
"12" HARDOX500 Products:
The HARDOX defended wear-resistant steel hardness level is divided into: the HARDOX defended by up to 400 the HARDOX defended by up to 450, the HARDOX defended by up to 500, the HARDOX defended by up to 550, the HARDOX defended 600 and HARDOX defended HiTuf. This means that you can always find the the HARDOX defended plate meet your specific needs.
HARDOX defended the 400 and HARDOX defended the 450 is a multi-purpose wear plate. Due to its high toughness, a good bending and welding performance, in some applications it can be used as a bearer purposes.
HARDOX defended 500 is a wear plate can be bent and welded, and can be applied on the wear resistance demanding areas.
The HARDOX defended 550 is an average hardness for 550HBW abrasion resistant steel, toughness and the HARDOX defended 500 the same, to be used in high wear occasions. Focused on the use of high-manganese steel castings or Brinell hardness of 500 wear plate users and manufacturers. When to upgrade to the product from HARDOX defended 500 steel plate, Brinell hardness increased 50 units, in the case of loss of steel plate toughness extended wear life. More information: HARDOX defended by up to 550 the HARDOX defended up to 550 in the Workshop uses: HARDOX defended by up to 500 steel plates typical of the hardness of 500 HBW thus able to withstand severe wear. It is very suitable for the working environment of strong wear, such as high strength ore and corrosive materials.
HARDOX defended the 600 is one of the world's most hard wear-resistant steel, hardness value of 600HBW. It is generally used in extremely serious occasion wear, and is mainly used to replace cast steel, chromium alloy cast iron surface hardening metal. Despite its high hardness, we still be able to be machined it, welding and cutting. Despite the very high hardness the HARDOX defended 600, but it still has a very high impact toughness.